Material Data Center is a leading international information system for the plastics industry. Material Data Center offers a comprehensive plastics database, calculation tools, CAE interfaces, a literature database and an application database. For more information about Material Data Center visit www.materialdatacenter.com.

This is the free Material Data Center Datasheet of FLEX NORYL™ Resin WCV072 - Asia - (PPE+TPE) - Saudi Basic Industries Corporation (SABIC)

Material Data Center offers the following functions for FLEX NORYL™ Resin WCV072 - Asia:
unit conversion, PDF datasheet print, comparison with other plastics, snap fit calculation, beam deflection calculation, CAE Interfaces

Check here, which other Flex Noryl datasheets, application examples or technical articles are available in Material Data Center

Use the following short links to get directly to the properties of interest in this datasheet:
加工/物理特性 - 机械性能 - 热性能 - 其它性能 - 加工推荐（注塑）
Any use of this information falls under the rules of our disclaimer.
材料文字说明
FLEX NORYL™ WCV072 resin is a flexible, non-reinforced extrusion grade of Polyphenylene Ether (PPE) + Thermoplastic Elastomer (TPE) with a Shore D Hardness rating of 72. FLEX NORYL WCV072 resin was developed for evaluation in automotive wire + cable applications requiring ISO6722 Class A or B. It exhibits ultra-thin wall capability, good scratch abrasion and pinch resistance, high dimensional stability, low shrinkage and warpage, very low water absorption, chemical resistance, and good dielectric strength. Processing is typically conducted on standard extrusion equipment, and UL 1581 testing is conducted on 2.0mm wire with 0.12mm X 20 stranded copper conductor.
加工/物理特性价值单位Test Standard
ISO数据
熔体体积流动速度, MVR 13 cm³/10min ISO 1133
温度 280 °C -
载荷 5 kg -
ASTM数据
熔融指数, MFI 13.8 g/10min ASTM D 1238
温度 280 °C -
负载 5 kg -
机械性能价值单位Test Standard
ISO数据
拉伸模量 1750 MPa ISO 527
屈服应力 44 MPa ISO 527
屈服伸长率 11 % ISO 527
断裂应力 42 MPa ISO 527
断裂伸长率 46 % ISO 527
弯曲模量 1740 MPa ISO 178
简支梁缺口冲击强度, +23°C 33 kJ/m² ISO 179/1eA
悬臂梁缺口冲击强度, +23°C, 4mm 36 kJ/m² ISO 180/1A
悬臂梁缺口冲击强度, -30°C, 4mm 6 kJ/m² ISO 180/1A
ASTM数据
拉伸模量 1710 MPa ASTM D 638
屈服应力 43 MPa ASTM D 638
断裂拉伸强度 41 MPa ASTM D 638
屈服伸长率 15 % ASTM D 638
断裂伸长率 83 % ASTM D 638
弯曲模量 1550 MPa ASTM D 790
悬臂梁缺口冲击强度, 1/8 in 309 J/m ASTM D 256
低温悬臂梁缺口冲击强度, Low-Temperature 67 J/m ASTM D 256
温度 -30 °C -
热性能价值单位Test Standard
ISO数据
热变形温度, 1.80 MPa 98 °C ISO 75-1/-2
维卡软化温度, B 114 °C ISO 306
维卡软化温度, 120°C/h 50N 117 °C ISO 306
ASTM数据
DTUL @ 264 psi 92 °C ASTM D 648
维卡温度 114 °C ASTM D 1525
其它性能价值单位Test Standard
吸水性 0.12 % 类似ISO 62
吸湿性 0.05 % 类似ISO 62
密度 1030 kg/m³ ISO 1183
密度 1030 kg/m³ ASTM D 792
加工推荐（注塑）价值单位Test Standard
螺杆转速 15 - 40 rpm -
典型数据
耐化学试剂
通用耐化学性
地区供应
亚太
权利义务的法律声明
Copyright Altair Engineering GmbH. Altair Engineering GmbH assumes no liability for the system to be free of errors. The user takes sole responsibility for the use of this data under the exclusion of every liability from Altair Engineering GmbH; this is especially valid for claims of compensation resulting from consequential damages. Altair explicitly points out that any decision about the application of materials must be double checked with the producer of this material. This includes all contents of this system. Copyright laws are applicable for the content of this system.
Created: Source: www.materialdatacenter.com


Material Data Center is provided by M-Base Engineering + Software GmbH. M-Base Engineering + Software GmbH assumes no liability for the system to be free of errors. Any decision about the application of materials must be double checked with the producer of this material.

Additional information about this material, like producer contact address, etc. can be found at www.materialdatacenter.com. For access to this extra information a registration is requested. Free online registration is available.